SabikThermotuf CF007IXP resin adalahsenyawa yang didasarkan pada polistiren yang mengandung serat kaca.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10230 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 8820 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 44 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 0.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8910 | MPa | ISO 527 |
| Tekanan Flexural | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8760 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 130 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 23 | J/m | ASTM D 256 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 2 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 97 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 92 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 5.26E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 5.33E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 97 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Kepadatan | 1.3 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.05 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 0.1 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 0.3 - 0.6 | % | ASTM D 955 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2009/07/28 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 250 | °C |
| Suhu depan - Zona 3 | 265 - 275 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 40 - 65 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/07/28 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!