SabikFaradex AS002 resin adalahsenyawa yang didasarkan pada resin acrylonitrile butadiene styrene yang mengandung stainless steel.
bahan termasuk: Konduktif listrik, EMI/RFI Shielding.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 42 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 39 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.2 | % | ASTM D 638 |
| Tekanan tarik, putus | 8.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2990 | MPa | ASTM D 638 |
| Tekanan Fleksural | 75 | MPa | ASTM D 790 |
| Modulus Flexural | 2810 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 39 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 37 | MPa | ISO 527 |
| Tekanan tarik, hasil | 2.2 | % | ISO 527 |
| Tekanan tarik, putus | 3.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2500 | MPa | ISO 527 |
| Tekanan Fleksural | 66 | MPa | ISO 178 |
| Modulus Flexural | 2500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 286 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 97 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 87 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.56E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.6E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 91 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.12 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 18 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 27 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.18 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.27 | % | ISO 294 |
| Kepadatan | 1.11 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+02 - 1.E+06 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+01 - 1.E+05 | Ohm | ASTM D 257 |
| Efektivitas Perisai @ 3mm | 40 - 55 | dB | Metode S-Plastics |
| Sumber GMD, terakhir diperbarui:02/27/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 - 0.1 | % |
| Suhu Peleburan | 240 - 255 | °C |
| Suhu depan - Zona 3 | 255 - 265 | °C |
| Tengah - Zona 2 Suhu | 230 - 245 | °C |
| Bagian belakang - Zona 1 Suhu | 210 - 220 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:02/27/2007 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
|
S-Plastics Faradex AS002.pdf |
|