| Tekanan tarik, yld, tipe I, 50 mm/menit |
63 |
MPa |
ASTM D638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit |
6 |
% |
ASTM D638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit |
> 70 |
% |
ASTM D638 |
| Tensile Modulus, 50 mm/min |
2350 |
MPa |
ASTM D638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm |
90 |
MPa |
ASTM D790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm |
2300 |
MPa |
ASTM D790 |
| Kekerasan, Rockwell R |
120 |
- |
ASTM D785 |
| Tekanan tarik, hasil, 50 mm/menit |
63 |
MPa |
ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit |
6 |
% |
ISO 527 |
| Tekanan tarik, putus, 50 mm/menit |
> 70 |
% |
ISO 527 |
| Modulus tarik, 1 mm/menit |
2350 |
MPa |
ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit |
90 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/menit |
2300 |
MPa |
ISO 178 |
| Kekerasan, Rockwell R |
120 |
- |
ISO 2039-2 |
| Dampak |
|
|
|
| Izod Dampak, tidak diukir, 23°C |
NB |
J/m |
ASTM D4812 |
| Izod Dampak, bertanduk, 23°C |
900 |
J/m |
ASTM D256 |
| Instrumen Dart Impact Energy @ puncak, 23°C |
65 |
J |
ASTM D3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C |
NB |
kJ/m2 |
ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C |
NB |
kJ/m2 |
ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C |
70 |
kJ/m2 |
ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C |
12 |
kJ/m2 |
ISO 180/1A |
| Termal |
|
|
|
| Vicat Softening Temperature, Tingkat B/50 |
144 |
°C |
ASTM D1525 |
| HDT, 0,45 MPa, 3,2 mm |
138 |
°C |
ASTM D648 |
| HDT, 1,82 MPa, 3,2 mm |
127 |
°C |
ASTM D648 |
| CTE, -40°C sampai 95°C, aliran |
7.00E-05 |
1/°C |
ASTM E831 |
| Konduktivitas Termal |
0.2 |
W/m-°C |
ASTM C177 |
| Konduktivitas Termal |
0.2 |
W/m-°C |
ISO 8302 |
| CTE, 23°C sampai 80°C, aliran |
7.00E-05 |
1/°C |
ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C |
Pas |
- |
IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 |
144 |
°C |
ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm |
138 |
°C |
ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm |
127 |
°C |
ISO 75/Af |
| FISIK |
|
|
|
| Gravitasi Spesifik |
1.2 |
- |
ASTM D792 |
| Penyerapan air, (23°C/Saturated) |
0.35 |
% |
ASTM D570 |
| Penyusutan jamur pada batang tarik, aliran |
0.5-0.7 |
% |
Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm |
0.5-0.7 |
% |
Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf |
7 |
g/10 menit |
ASTM D1238 |
| Kepadatan |
1.2 |
g/cm3 |
ISO 1183 |
| Absorpsi air, (23°C/jenuh) |
0.35 |
% |
ISO 62-1 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg |
6 |
cm3/10 menit |
ISO 1133 |
| Optik |
|
|
|
| Transmisi cahaya, 2,54 mm |
88-90 |
% |
ASTM D1003 |
| Kabut, 2,54 mm |
<0.8 |
% |
ASTM D1003 |
| Indeks Refraksi |
1.586 |
- |
ASTM D542 |
| Indeks Refraksi |
1.586 |
- |
ISO 489 |
| Listrik |
|
|
|
| Resistivitas Volume |
>1.E+15 |
Ω.cm |
ASTM D257 |
| Kekuatan dielektrik, 1,6 mm |
27 |
kV/mm |
ASTM D149 |
| Permittivitas relatif, 60 Hz |
3 |
- |
ASTM D150 |
| Permittivitas Relatif, 1 MHz |
3 |
- |
ASTM D150 |
| Faktor Dissipasi, 60 Hz |
0.001 |
- |
ASTM D150 |
| Faktor Dissipasi, 1 MHz |
0.01 |
- |
ASTM D150 |
| Resistivitas Volume |
>1.E+15 |
Ω.cm |
IEC 60093 |
| Kekuatan dielektrik, 1,6 mm |
27 |
kV/mm |
IEC 60243-1 |
| Permittivitas relatif, 60 Hz |
3 |
- |
IEC 60250 |
| Permittivitas Relatif, 1 MHz |
3 |
- |
IEC 60250 |
| Faktor Dissipasi, 60 Hz |
0.001 |
- |
IEC 60250 |
| Faktor Dissipasi, 1 MHz |
0.01 |
- |
IEC 60250 |
| Karakteristik Api |
|
|
|
| UL Yellow Card Link |
E207780-101295396 |
- |
- |
| UL diakui, 94V-2 Flame Class Rating |
1.6 |
mm |
UL 94 |
|
|
|
|