XHT4141 adalah copolymer polikarbonat aliran tinggi, panas tinggi.
Aku tidak tahu.Properti
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 77 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 69 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2730 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2600 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 78 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 67 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2750 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 93 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 76 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 72 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 183 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 174 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 165 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | P | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 183 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 181 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 173 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Af |
Pengolahan
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 355 | °C |
| Suhu Nozzle | 305 - 350 | °C |
| Suhu depan - Zona 3 | 310 - 355 | °C |
| Tengah - Zona 2 Suhu | 310 - 345 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 330 | °C |
| Suhu Cetakan | 95 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 90 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:09/27/2006 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
Lexan Resin XHT4141.pdf |
|