SabikStat-konLexan_SP7750 resinadalah serat karbon diperkuat untuk perisai EMI/RFI.
Aku tidak tahu.Properti
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 136 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 151 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 213 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 20960 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 20060 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 267 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 7 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 101 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 95 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 102 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 96 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0 - 0.1 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.05 - 0.15 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 0.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 5.E+02 | Ohm | ASTM D 257 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
| Kerusakan statis, 5000V hingga <50V | 0.01 | < detik | FTMS101B |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.19 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:03/15/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Suhu Peleburan | 270 - 310 | °C |
| Suhu Nozzle | 270 - 300 | °C |
| Suhu depan - Zona 3 | 270 - 300 | °C |
| Tengah - Zona 2 Suhu | 270 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 275 | °C |
| Suhu Cetakan | 50 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 35 - 75 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/15/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Lexan_SP7750.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|