SabikStat-konLexan_LCF1506 resinadalah 15% serat karbon, 6% PTFE diperkuat polikarbonat.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 111 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 111 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4.1 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 160 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 154 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9080 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 8410 | MPa | ASTM D 790 |
| K-faktor xE-10, PV = 2000 psi-fpm vs Baja | 1000 | - | Metode S-Plastics |
| Koefisien gesekan pada baja, statis | 0.41 | - | ASTM D 1894 |
| Koefisien gesekan pada baja,kinetik | 0.19 | - | ASTM D 1894 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 11 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 141 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 144 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 139 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.05 - 0.15 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.2 - 0.3 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+04 | Ohm | ASTM D 257 |
| Kerusakan statis, 5000V hingga <50V | 0.01 | < detik | FTMS101B |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.49 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:03/15/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 315 | °C |
| Suhu Nozzle | 290 - 315 | °C |
| Suhu depan - Zona 3 | 290 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 295 | °C |
| Suhu Cetakan | 70 - 105 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/15/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Lexan_LCF1506.pdf |
|