SabikStat-konLexan_JK2500 resinadalah 20% serat karbon diperkuat, non-halogenasi merah bebas fosfor, aliran tinggi FR PC+ABS
untuk pelindung EMI/RFI. SE 21 dB pada 1,5 mm.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 11030 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 112 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9230 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 11130 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 110 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 110 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 10090 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 224 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 14 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 111 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 98 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 93 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 96 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.26E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.3E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.7E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 100 | °C | ISO 306 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 00.06 - 0.15 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 25 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+04 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.99 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui: 29/10/2002 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Suhu Peleburan | 270 - 310 | °C |
| Suhu Nozzle | 270 - 300 | °C |
| Suhu depan - Zona 3 | 270 - 300 | °C |
| Tengah - Zona 2 Suhu | 270 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 275 | °C |
| Suhu Cetakan | 50 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 35 - 75 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui: 29/10/2002 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Lexan_JK2500.pdf |
|