SabikThermocompLexan_SML5897resin adalah PC diperkuat 40% serat karbon untuk digunakan dalam aplikasi modulus tinggi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 148 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 148 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.1 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 210 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 18270 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 411 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 7 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 151 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 147 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 142 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.6E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.14E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 3.6E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 4.68E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.4 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | - 0.1 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.14 - 0.27 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 7.9 | g/10 menit | ASTM D 1238 |
| Tingkat Volume Peleburan, MVR pada 300°C/2,16 kg | 9 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 3.E+03 | Ohm | ASTM D 257 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 2 | Kode PLC | UL 746A |
| Kerusakan statis, 5000V hingga <50V | 0.01 | < detik | FTMS101B |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.99 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:07/31/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 315 | °C |
| Suhu Nozzle | 290 - 315 | °C |
| Suhu depan - Zona 3 | 290 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 295 | °C |
| Suhu Cetakan | 70 - 105 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:07/31/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
Lexan_SML5897.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|