SabikThermocompLexan_LGN2000Aresin adalah 20% kaca diperkuat PC, aliran tinggi. UL dinilai V-0.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 81 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4.9 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 124 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5030 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 400 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 14 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 141 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 135 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.34E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 2.52E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 5.58E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.35 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.15 - 0.25 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.25 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 20.7 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.49 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:06/29/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 295 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:06/29/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Lexan_LGN2000A.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|