SabikThermocompLexan_BFL2200resin adalah...
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 5.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 59 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 2590 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 84 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2220 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 5.4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 47.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 0 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 0 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 547 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 159 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 125 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.83E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.86E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.13E+01 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.89E+01 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 172 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.74 - 0.76 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 36.1 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 35 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:12/01/2005 |
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |