SabikLexanEkspor dari Indonesiaresin adalahLexan* EXRL0344 resin kopolymer silikon silikon polikarbonat (PC) adalah jenis cetakan injeksi transparan dengan transparansi yang dioptimalkan dan sifat kabut yang berkurang. This resin offers low temperature (-10 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resinsLexan Pengembangan
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 134 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2160 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 59 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.1 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 119.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2530 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 89 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2240 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 736 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -10°C | 584 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -20°C | 573 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 69 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 46 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 18 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 61 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 21 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat A/50 | 137 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 118 | °C | ASTM D 648 |
| CTE, -40°C sampai 60°C, aliran | 6.19E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 60°C, xflow | 6.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.19E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 139 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 20 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 19 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 87 | % | ASTM D 1003 |
| Kabut | 1.2 | % | ASTM D 1003 |
| Sumber GMD, terakhir diperbarui:11/09/2006 | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 3 - 4 | jam | |
| Waktu pengeringan (kumulatif) | 48 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 295 - 315 | °C | |
| Suhu Nozzle | 290 - 310 | °C | |
| Suhu depan - Zona 3 | 295 - 315 | °C | |
| Tengah - Zona 2 Suhu | 280 - 305 | °C | |
| Bagian belakang - Zona 1 Suhu | 270 - 295 | °C | |
| Suhu Cetakan | 70 - 95 | °C | |
| Tekanan Belakang | 0.3 - 0.7 | MPa | |
| Kecepatan sekrup | 40 - 70 | rpm | |
| Menembak untuk ukuran silinder | 40 - 60 | % | |
| Kedalaman ventilasi | 0.025 - 0.076 | mm | |
| Sumber GMD, terakhir diperbarui:11/09/2006 | |||
| Nilai properti ini tidak dimaksudkan untuk tujuan spesifikasi. | |||
| Silakan periksa dengan (kantor penjualan lokal) untuk ketersediaan di wilayah Anda | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. | |||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0344.pdf |
|