S-Plastics LexanFL1600Pengurangan Berat Berbagai Pada 0,250 " (6,35 mm) Dinding.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| busa - MEKANIS 6.4 mm Wt Pengurangan | 10 | % | - |
| Tekanan tarik, hasil, 6,35 mm | 48 | MPa | ASTM D 638 |
| Tekanan tarik, putus, 6,35 mm | 5.2 | % | ASTM D 638 |
| Tensile Modulus, 6,4 mm | 2440 | MPa | ASTM D 638 |
| Tekanan lentur, hasil, 6,4 mm | 89 | MPa | ASTM D 790 |
| Flexural Modulus, 6,4 mm | 2750 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| BUMEN - Dampak 6.4 mm Wt Pengurangan | 10 | % | - |
| Izod Dampak, tidak diukir, 23°C | 747 | J/m | ASTM D 4812 |
| Terjatuh Dart Dampak, 23°C | 56 | J | Metode S-Plastics |
| Termal | Nilai | Satuan | Standar |
| BUMEN - PEMERINTAH 6.4mm Wt Pengurangan | 10 | % | - |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 126 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 5.04E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.15 | J/g-°C | ASTM C 351 |
| FISIK | Nilai | Satuan | Standar |
| busa - PHYSICAL 6.4mm Wt Pengurangan | 10 | % | - |
| Gravitasi Spesifik | 1.25 | - | ASTM D 792 |
| Gravitasi spesifik, cetakan busa | 1.13 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.33 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 6,4 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| busa - Listrik 6.4 mm Wt Pengurangan | 20 | % | - |
| Resistivitas Volume | 2.8E+17 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.1E+17 | Ohm | ASTM D 257 |
| Permittivitas relatif, 100 Hz | 2.45 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.44 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.007 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.0042 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:08/07/1989 | |||
| Parameter | ||
| Membentuk busa struktural | Nilai | Satuan |
| Agen Blowing, Sistem Fisik | Gas nitrogen | - |
| Agen Blowing, Sistem Kimia | FLC298 | - |
| Waktu Pengeringan (Agen Bertiup) | 4 | jam |
| Suhu Pengeringan (Agen Bertiup) | 105 | °C |
| Jangkauan konsentrasi (Agen Blowing) | 3 - 5 | % |
| Konsentrasi yang Disarankan (Agen Blowing) | 1.5 | % |
| Suhu pengeringan (resin) | 120 | °C |
| Waktu pengeringan (resin) | 3 - 4 | jam |
| Waktu pengeringan (resin, kumulatif) | 48 | jam |
| Suhu Peleburan | 290 - 310 | °C |
| Suhu Nozzle | 270 - 295 | °C |
| Suhu Depan | 290 - 305 | °C |
| Suhu Rata-rata | 290 - 305 | °C |
| Suhu Belakang | 255 - 280 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Sumber GMD, terakhir diperbarui:08/07/1989 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan FL1600.pdf |
|