SabikLexanBentuk-bentuknya:resin adalahresin polikarbonat, MVR (300C/1.2kg) 2 cm3/10min, viskositas tinggi, bercabang, ekstrusi, pelepasan cetakan, UV stabil, transparan, tembus dan warna buram.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 70 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 75 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 55 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 149 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 150 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.5 - 0.7 | % | Metode S-Plastics |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 2 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 300°C/2,16 kg | 4 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:2010/01/20 | |||
| Parameter | ||
| Ekstrusi lembaran multiwall | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Barel - Zona 1 Suhu | 260 - 300 | °C |
| Barel - Zona 2 Suhu | 260 - 290 | °C |
| Barel - Zona 3 Suhu | 260 - 290 | °C |
| Suhu Hopper | 100 - 120 | °C |
| Suhu adaptor | 240 - 280 | °C |
| Suhu mati | 240 - 300 | °C |
| Suhu Peleburan | 260 - 300 | °C |
| Suhu Kalibrator | 50 - 100 | °C |
| Sumber GMD, terakhir diperbarui:2010/01/20 | ||
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Lexan EXRL0742.pdf |