SabikLexanEXRL0722resin adalahKualitas optik, resin PC kemurnian tinggi untuk aplikasi CD/DVD dan BD pada waktu siklus pendek
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | > 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2350 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 40 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 12 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 132 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyerapan air, keseimbangan, 23C | 0.35 | % | ASTM D 570 |
| Penyusutan jamur pada batang tarik, aliran (2) (5) | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/1,2 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/1,2 kg | 9 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi cahaya, 2,54 mm | > 90 | % | ASTM D 1003 |
| Kabut, 2,54 mm | <0.7 | % | ASTM D 1003 |
| Indeks Refraksi | 1.586 | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Permittivitas Relatif, 1 MHz | 3 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | IEC 60250 |
| Sumber GMD, terakhir diperbarui:2010/05/17 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 370 | °C |
| Suhu Nozzle | 340 - 370 | °C |
| Suhu depan - Zona 3 | 350 - 380 | °C |
| Tengah - Zona 2 Suhu | 320 - 340 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 290 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 75 - 95 | °C |
| Sumber GMD, terakhir diperbarui:2010/05/17 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0722.pdf |
|