SabikLexanEXRL0468resin adalahResin PC berkualitas optik aliran tinggi, kemurnian tinggi untuk aplikasi CD/DVD
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2410 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2240 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2400 | MPa | ISO 178 |
| Kekerasan, H358/30 | 100 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 550 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 46 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 140 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 120 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 140 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 142 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 135 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.05 - 0.07 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/1,2 kgf | 11.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.19 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/1,2 kg | 11 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:02/26/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 330 | °C |
| Suhu Nozzle | 305 - 330 | °C |
| Suhu depan - Zona 3 | 305 - 330 | °C |
| Tengah - Zona 2 Suhu | 295 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 310 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 60 - 200 | rpm |
| Sumber GMD, terakhir diperbarui:02/26/2008 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0468.pdf |
|