SabikLexanEXRL0436resin adalahKelas tahan api viskositas menengah dengan penampilan berkilau logam.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 10 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2650 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 110 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 128 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.24 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 9 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:07/11/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 280 - 310 | °C |
| Suhu Nozzle | 270 - 290 | °C |
| Suhu depan - Zona 3 | 280 - 310 | °C |
| Tengah - Zona 2 Suhu | 270 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Sumber GMD, terakhir diperbarui:07/11/2007 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0436.pdf |
|