SabikLexanEXRL0423resin adalahsebuah copolymer polikarbonat aliran tinggi, panas tinggi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 70 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 90 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2600 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 110 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2550 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 90 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2450 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 115 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 161 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 155 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 145 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 160 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 162 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 155 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
| Dimulai Kabut Berlogam | 155 | °C | Metode S-Plastics |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 330°C/2,16 kgf | 46 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.23 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 330°C/2,16kg | 43 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/04/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 125 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 355 | °C |
| Suhu Nozzle | 285 - 350 | °C |
| Suhu depan - Zona 3 | 290 - 355 | °C |
| Tengah - Zona 2 Suhu | 280 - 345 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 330 | °C |
| Suhu Cetakan | 85 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 90 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/04/2007 | ||