SabikLexanEXRL0422resin adalah103R untuk aplikasi las laser
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 120 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 127 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:07/11/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 320 | °C |
| Suhu Nozzle | 280 - 310 | °C |
| Suhu depan - Zona 3 | 290 - 320 | °C |
| Tengah - Zona 2 Suhu | 280 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 300 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 120 | °C |
| Sumber GMD, terakhir diperbarui:07/11/2007 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0422.pdf |
|