SabikLexanFL900Presin adalah Foamable LEXAN, berbagai pengurangan berat pada 6,4 mm. Menawarkan kapasitas beban pada suhu tinggi., Menggabungkan kekakuan, dampak & ketahanan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 42 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 50 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Dampak Gardner (GE) | 50 | J | Metode S-Plastics |
| Termal | Nilai | Satuan | Standar |
| Panas spesifik | 0.28 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.15 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 3.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 0.95 | - | ASTM D 792 |
| Kandungan pengisi | 5 | % | ASTM D 229 |
| Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 10 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Kabut | NA | % | ASTM D 1003 |
| Indeks Refraksi | NA | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Permittivitas relatif, 100 Hz | 2.4 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.3 | - | IEC 60250 |
| Faktor Dissipasi, 100 Hz | 0.0029 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 6 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 6 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:02/25/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 320 | °C |
| Suhu Nozzle | 290 - 320 | °C |
| Suhu depan - Zona 3 | 290 - 320 | °C |
| Tengah - Zona 2 Suhu | 280 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 295 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Sumber GMD, terakhir diperbarui:02/25/2003 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan FL900P.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|
|