SabikLexanEXRL0149resin adalahLapisan warna transparan PC/SLX untuk bisnis film dan lembaran khusus.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 72 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2320 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 99 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2420 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 69 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6.2 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 118 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 92 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2310 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 975 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 390 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 86 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 71 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 13 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 89 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 127 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 123 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 5.1 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.21 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 4 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui: 02/21/2006 | |||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXRL0149.pdf |
|