SabikLexanEksplorasiresin adalahCopolymer PC-Siloxane dengan proses yang sangat baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1720 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 79 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1990 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 88 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2270 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2090 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 801 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 694 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 62 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 61 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 70 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 60 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 136 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.02E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 6.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.3E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 7 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Resistivitas Volume | 1.7E+17 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 4.1E+17 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas Relatif, 1 MHz | 2.6 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.0094 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:10/31/2002 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 295 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:10/31/2002 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan EXL6414.pdf |
|