SabikLexanML5472resin adalahtahan sterilisasi gamma. panas tinggi (PPC). tersedia hanya dalam warna alami. pelepasan jamur internal.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 71 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 122 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2090 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2020 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 85 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 122 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 7 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2260 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 66 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2120 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 640 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 144 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 577 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 149 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 73 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 13 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 11 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 160 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 143 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 160 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 151 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 9.18E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.21 | W/m-°C | ASTM C 177 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 155 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 132 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 125 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 125 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 125 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
| Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.16 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.7 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 3 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.16 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.35 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 3 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 85 | % | ASTM D 1003 |
| Kabut | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.6 | - | ASTM D 542 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >2.6E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 20.2 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.15 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0012 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.024 | - | ASTM D 150 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-2 Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:03/06/2008 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 360 | °C |
| Suhu Nozzle | 330 - 355 | °C |
| Suhu depan - Zona 3 | 340 - 360 | °C |
| Tengah - Zona 2 Suhu | 325 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/06/2008 | ||
| Nilai properti ini tidak dimaksudkan untuk tujuan spesifikasi. | ||
| Silakan periksa dengan (kantor penjualan lokal) untuk ketersediaan di wilayah Anda | ||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
||
| (2) Hanya data tipikal untuk tujuan seleksi. | ||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | ||
| (4) Pengukuran internal menurut standar UL. | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |