SabikLexanML4588resin adalahKelas extrusi dan extrusi blowmolding untuk aplikasi pesawat terbang.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2480 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 720 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 59 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 132 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.21 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 2.5 | g/10 menit | ASTM D 1238 |
| Karakteristik Api | Nilai | Satuan | Standar |
| FAR 25.853 A/B | (A), 1, (I) | - | FAR 25.853 |
| Sumber GMD, terakhir diperbarui:01/04/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 320 - 345 | °C |
| Suhu Nozzle | 315 - 340 | °C |
| Suhu depan - Zona 3 | 320 - 345 | °C |
| Tengah - Zona 2 Suhu | 310 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 300 - 320 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan ML4588.pdf |
|