SabikLexanRL7503resin adalah Impak dimodifikasi PC/siloxane copolymer.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1720 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 88 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2270 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3200 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 800 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 700 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 62 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 60 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 63 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 74 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 60 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 147 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 136 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.02E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 6.9E-02 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.3E-02 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 142 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.7 - 0.9 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.06 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 7 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Resistivitas Volume | 1.7E+17 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 4.1E+17 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas Relatif, 1 MHz | 2.6 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.0094 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:04/02/2004 | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. |
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan RL7503.pdf |
|