S-Plastics LexanSLX2531Tresin adalahCopolymer PC transparan tahan cuaca untuk blowmolding/extrusion.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 106 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 101 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2400 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 98 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2240 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 848 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 141 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 74 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 70 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 126 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.02E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.36E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.02E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.36E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 3 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 2 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-2 (3) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:09/20/2006 | |||
| • PERHATIAN: Untuk penundaan produksi dua jam atau lebih, kurangi titik pengaturan suhu menjadi 150°C (300°F). | ||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 115 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Kandungan Kelembaban Minimal | 0.01 | % |
| Suhu Peleburan (Parison) | 265 - 275 | °C |
| Barel - Zona 1 Suhu | 260 - 275 | °C |
| Barel - Zona 2 Suhu | 260 - 275 | °C |
| Barel - Zona 3 Suhu | 260 - 275 | °C |
| Barel - Zona 4 Suhu | 260 - 275 | °C |
| Adaptor - Zona 5 Suhu | 260 - 275 | °C |
| Kepala - Zona 6 - Suhu puncak | 260 - 275 | °C |
| Kepala - Zona 7 - Suhu bawah | 260 - 275 | °C |
| Kecepatan sekrup | 15 - 50 | rpm |
| Suhu Cetakan | 65 - 95 | °C |
| Suhu mati | 270 - 280 | °C |
| Sumber GMD, terakhir diperbarui:09/20/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan SLX2531T.pdf |
|