SabikLexanEXL4016resin adalah6% GF diperkuat copolymer polycarbonate-siloxane opaque, untuk peningkatan kekakuan dengan kekuatan dampak yang baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3300 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 53 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4.4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 14 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 91 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2830 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 493 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 188 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 40 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat A/50 | 146 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 137 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.1E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 147 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 147 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.2 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 6 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.12 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.46 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 5 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:02/14/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 330 | °C |
| Suhu Nozzle | 305 - 325 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 300 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:02/14/2005 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan EXL4016.pdf |
|