SabikLexanRL7301resin adalah PC serbaguna dengan viskositas rendah yang memiliki tingkat spesies ionik yang rendah.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 68 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 694 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 62 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 129 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 6.84E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.19 | W/m-°C | ASTM C 177 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
| Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
| Penyerapan air, keseimbangan, 100°C | 0.58 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 17.5 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.586 | - | ASTM D 542 |
| Sumber GMD, terakhir diperbarui:01/04/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu Nozzle | 275 - 300 | °C |
| Suhu depan - Zona 3 | 280 - 305 | °C |
| Tengah - Zona 2 Suhu | 270 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/04/2000 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan RL7301.pdf |
|