SabikLexanRL7234resin adalah Resin PC Terbatas untuk Aplikasi Pakaian Matahari Warna Khusus.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 72 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2270 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 |
| Kemurnian, partikel per gram > 50 mikron | 1 | - | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 61 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 71 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 140 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 918 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 84 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 74 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 14 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 88 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 19 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 150 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 139 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 128 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.74E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.74E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 144 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 139 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 126 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.7 - 0.9 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 7.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 5 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:08/26/2003 | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. |
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan RL7234.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|
|