SabikLexanRL6842resin adalah SINGLE LOT DATA. kinerja superior. resin SP dimodifikasi untuk dampak suhu rendah yang sangat baik. pelepasan cetakan internal.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2060 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, -20°C | 694 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 640 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 640 | J/m | ASTM D 256 |
| Dampak Instrumen, Energi @ puncak, -20°C | 48 | J | ASTM D 3763 |
| Energi Dampak Instrumen @ puncak, -40°C | 35 | J | ASTM D 3763 |
| FISIK | Nilai | Satuan | Standar |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 16.5 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:01/04/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Suhu Peleburan | 260 - 305 | °C |
| Suhu Nozzle | 255 - 300 | °C |
| Suhu depan - Zona 3 | 260 - 305 | °C |
| Tengah - Zona 2 Suhu | 250 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 280 | °C |
| Suhu Cetakan | 50 - 80 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 35 - 75 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/04/2000 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan RL6842.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|
|