SabikLexanSLX1431T resin adalahCampuran kopolymer PC viskositas menengah dengan stabilisasi UV yang ditingkatkan dan agen pelepasan tambahan.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 73 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | > 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2450 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2450 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 820 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 100 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 80 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 65 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 149 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 134 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 139 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 9 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 89 | % | ASTM D 1003 |
| Kabut | 0.2 | % | ASTM D 1003 |
| Sumber GMD, terakhir diperbarui:09/29/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 280 - 310 | °C |
| Suhu Nozzle | 270 - 290 | °C |
| Suhu depan - Zona 3 | 280 - 310 | °C |
| Tengah - Zona 2 Suhu | 270 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Sumber GMD, terakhir diperbarui:09/29/2005 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lexan SLX1431T.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|
|