SabikLexanRL6571resin adalah SINGLE LOT DATA (L37313): 20% kelas SP bertulang kaca. warna M73445.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 89 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3.4 | % | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 144 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5010 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 66 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 7 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 123 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.35 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.24 - 0.45 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 6.3 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Suhu Peleburan | 270 - 310 | °C |
| Suhu Nozzle | 270 - 300 | °C |
| Suhu depan - Zona 3 | 270 - 300 | °C |
| Tengah - Zona 2 Suhu | 270 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 275 | °C |
| Suhu Cetakan | 50 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 35 - 75 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Lexan RL6571.pdf |