SabikLexanSD9705 resin adalahPC Copolymer visosity tinggi, asap rendah, resin tahan api
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 72 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 73 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 102 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2610 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 115 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2500 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 74 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 76 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 109 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 107 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2320 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 194 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 112 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 80 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 17 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 17 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eU |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 24 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 140 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.7E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.7E-06 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-06 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, perkiraan maksimum | 125 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 139 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 117 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 5 | g/10 menit | ASTM D 1238 |
| Rasio Poisson | 0.4 | - | ASTM D 638 |
| Kepadatan | 1.34 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.28 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.11 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 4 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 300°C/5,0 kg | 16 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| OSU total pelepasan panas (tes 2 menit) | < 55 | kW-menit/m2 | FAR 25.853 |
| Kecepatan pelepasan panas puncak OSU (tes 5 menit) | < 55 | kW/m2 | FAR 25.853 |
| Vertikal Burn a (60s) melewati di | 2.4 | detik | FAR 25.853 |
| Vertikal Burn b (12s) melewati | 0.5 | detik | FAR 25.853 |
| Densitas asap, api, Dmax | < 25 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:07/14/2008 | |||
| Parameter | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 3 - 4 | jam | |
| Waktu pengeringan (kumulatif) | 48 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 280 - 305 | °C | |
| Suhu Nozzle | 275 - 300 | °C | |
| Suhu depan - Zona 3 | 280 - 305 | °C | |
| Tengah - Zona 2 Suhu | 270 - 295 | °C | |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C | |
| Suhu Cetakan | 70 - 95 | °C | |
| Tekanan Belakang | 0.3 - 0.7 | MPa | |
| Kecepatan sekrup | 40 - 70 | rpm | |
| Menembak untuk ukuran silinder | 40 - 60 | % | |
| Kedalaman ventilasi | 0.025 - 0.076 | mm | |
| Sumber GMD, terakhir diperbarui:07/14/2008 | |||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |