SabikLexanML3512resin adalahviskositas tinggi, 20% serat kaca pendek diperkuat, tingkat tahan api, terutama cocok untuk aplikasi listrik.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 5 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3000 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3000 | MPa | ISO 178 |
| Kekerasan, H358/30 | 120 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell L | 100 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Charpy Impact, tidak diukir, 23°C | 80 | kJ/m2 | ISO 179/2C |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | 40 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 40 | kJ/m2 | ISO 179/1eU |
| Charpy Impact, bertanduk, 23°C | 8 | kJ/m2 | ISO 179/2C |
| Charpy Impact, bertanduk, -20°C | 6 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.22 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 3.7E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 145 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 147 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 144 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 140 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.3 - 0.5 | % | Metode S-Plastics |
| Kepadatan | 1.35 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.29 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.12 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 5 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+14 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.011 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-1 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 32 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:05/18/1989 | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 2 - 4 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 290 - 320 | °C | |
| Suhu Nozzle | 280 - 310 | °C | |
| Suhu depan - Zona 3 | 290 - 320 | °C | |
| Tengah - Zona 2 Suhu | 280 - 310 | °C | |
| Bagian belakang - Zona 1 Suhu | 270 - 300 | °C | |
| Suhu Hopper | 60 - 80 | °C | |
| Suhu Cetakan | 80 - 120 | °C | |
| Sumber GMD, terakhir diperbarui:05/18/1989 | |||
| Nilai properti ini tidak dimaksudkan untuk tujuan spesifikasi. | |||
| Silakan periksa dengan (kantor penjualan lokal) untuk ketersediaan di wilayah Anda | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi |
|||
 |
|||
| Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. | |||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Lexan ML3512.pdf |
|