SabikLexanML104R resin adalahLexan ML104R resin adalah viskositas tinggi multi purpose grade. FDA sesuai kontak makanan dalam warna terbatas.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 68 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 135 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2310 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 70 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 120 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Kekerasan, H358/30 | 95 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 907 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 139 | J/m | ASTM D 256 |
| Dampak tarik, tipe S | 630 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 169 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 65 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 65 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 95 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, bertanduk, 23°C | 35 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 6.84E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.19 | W/m-°C | ASTM C 177 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 140 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 138 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 127 | °C | ISO 75/Ae |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
| Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.35 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 100°C | 0.58 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 7 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 4 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi cahaya, 2,54 mm | 88 | % | ASTM D 1003 |
| Kabut, 2,54 mm | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.586 | - | ASTM D 542 |
| Indeks Refraksi | 1.586 | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 14.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.17 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.96 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.7 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.7 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Glow Wire Flammability Index 850°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 25 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:2009/07/20 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 330 | °C |
| Suhu Nozzle | 305 - 325 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 300 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:2009/07/20 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan ML104R.pdf |
|