SabikLexanML7680 resin
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 99 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 153 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6610 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 92 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 120 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 24 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1121 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 67 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 5 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 165 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 151 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 146 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 2.16E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.13 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.22 | W/m-°C | ASTM C 177 |
| Indeks suhu relatif, Elec | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.43 | - | ASTM D 792 |
| Volume Spesifik | 0.69 | cm3/g | ASTM D 792 |
| Kepadatan | 1.44 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.26 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 5 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 300°C/5,0 kgf | 19 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.7 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.35 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.31 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0011 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.007 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 7 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 5 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL diakui, 94V-1 Flame Class Rating (3) | 1.47 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 2.99 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:08/11/2008 | |||
| Parameter | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 3 - 4 | jam | |
| Waktu pengeringan (kumulatif) | 48 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 315 - 340 | °C | |
| Suhu Nozzle | 310 - 330 | °C | |
| Suhu depan - Zona 3 | 315 - 340 | °C | |
| Tengah - Zona 2 Suhu | 305 - 325 | °C | |
| Bagian belakang - Zona 1 Suhu | 295 - 315 | °C | |
| Suhu Cetakan | 80 - 115 | °C | |
| Tekanan Belakang | 0.3 - 0.7 | MPa | |
| Kecepatan sekrup | 40 - 70 | rpm | |
| Menembak untuk ukuran silinder | 40 - 60 | % | |
| Kedalaman ventilasi | 0.025 - 0.076 | mm | |
| Sumber GMD, terakhir diperbarui:08/11/2008 | |||
| Nilai properti ini tidak dimaksudkan untuk tujuan spesifikasi. | |||
| Silakan periksa dengan (kantor penjualan lokal) untuk ketersediaan di wilayah Anda | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan ML7680.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|
|