SabikLexanHPB3144resin adalahAliran standar, transparan, resin kopolymer polikarbonat kemurnian tinggi dengan permeabilitas oksigen yang rendah dan tingkat transmisi uap air.Manajemen perubahan perawatan kesehatan, biokompatibel (ISO 10993 atau USP Kelas VI), sesuai dengan kontak makanan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 80 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 70 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2900 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2600 | MPa | ASTM D 790 |
| Kekerasan, Rockwell L | 108 | - | ASTM D 785 |
| Kekerasan, Rockwell M | 93 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 40 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2450 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 108 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2450 | MPa | ISO 178 |
| Kekerasan, H358/30 | 128 | MPa | ISO 2039-1 |
| Tes Kekerasan Pensil, 1kgf | H | - | ASTM D 3363 |
| kedalaman goresan Erichson, 6N | 14 | Mikrometer | Metode S-Plastics |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 30 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 30 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 30 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | 45 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 47 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 139 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 119 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.4 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 140 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 131 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 118 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.85 | cm3/g | ASTM D 792 |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.28 | % | ASTM D 570 |
| Absorpsi air, 50% RH, keseimbangan | 0.13 | % | ASTM D 570 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.04 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 14.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.27 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 13 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | <0.8 | % | ASTM D 1003 |
| Indeks Refraksi | 1.584 | - | ASTM D 542 |
| Indeks Refraksi | 1.584 | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.8 | - | ASTM D 150 |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Sumber GMD, terakhir diperbarui:06/26/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Sumber GMD, terakhir diperbarui:06/26/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan HPB3144.pdf |
|