SabikLexanEXL1182Tresin adalahPolycarbonate (PC) siloxane copolymer resin adalah UV stabil, enhanced release transparan injeksi cetakan (IM) kelas. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. resin Lexan EXL1182T adalah produk pelepasan UV stabil, ditingkatkan tersedia dalam warna transparan dan buram dan mungkin menjadi kandidat yang sangat baik untuk berbagai aplikasi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 57 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 117.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2260 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2240 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 57 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 56 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 119.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2340 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 89 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2140 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 736 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 618 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 74 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 47 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 24 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 61 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 17 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat A/50 | 138 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 7.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 7.64E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 7.48E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.64E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 139 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 20 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.19 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.24 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 19 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:11/16/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 295 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:11/16/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan EXL1182T.pdf |
|