SabikLexanEXL1033Cresin adalahPolycarbonate (PC) siloxane copolymer resin adalah aliran rendah, kualitas UV stabil yang dirancang untuk (co) ekstrusi.Resin ini menawarkan ketangguhan suhu rendah (-30C) dan karakteristik pengolahan ekstrusi yang sangat baikTersedia dalam warna transparan dan tidak transparan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 61 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 114 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 98 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Kekerasan, Rockwell L | 88 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 64 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6.2 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 142.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 2270 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 893 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 720 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 75 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 66 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 23 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 84 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 28 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 145 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 135 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.06E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.67E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.06E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.67E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 141 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 119 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 6.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | NB0.18 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | NB0.01 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 86 | % | ASTM D 1003 |
| Kabut | 1.7 | % | ASTM D 1003 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL diakui, 94V-2 Flame Class Rating (3) | 2.5 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:03/26/2008 | |||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Barel - Zona 1 Suhu | 250 - 290 | °C |
| Barel - Zona 2 Suhu | 245 - 270 | °C |
| Barel - Zona 3 Suhu | 225 - 255 | °C |
| Suhu adaptor | 225 - 255 | °C |
| Suhu mati | 240 - 260 | °C |
| Temperature Roll Stack - Atas | 75 - 115 | °C |
| Temperature Roll Stack - Pertengahan | 80 - 125 | °C |
| Roll Stack Temp - Bagian bawah | 120 - 145 | °C |
| Sumber GMD, terakhir diperbarui:03/26/2008 | ||