SabikLexanDMX6014resin adalahresin ini menggabungkan ketahanan goresan yang sangat baik (ketat F-pencil) dengan
ketebalan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 45 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 45 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2200 | MPa | ASTM D 790 |
| Kekerasan, Rockwell L | 90 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 117 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 48 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2150 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2150 | MPa | ISO 178 |
| Tes Kekerasan Pensil, 1kgf | F | - | ASTM D 3363 |
| kedalaman goresan Erichson, 6N | 14 | Mikrometer | Metode S-Plastics |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 220 | J/m | ASTM D 256 |
| Dampak Multiaxial | 55 | J | ISO 6603 |
| Izod Impact, bernotas 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 97 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/120 | 118 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.15 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 12 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 10 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:03/06/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 110 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 240 - 280 | °C |
| Suhu depan - Zona 3 | 250 - 290 | °C |
| Tengah - Zona 2 Suhu | 250 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Sumber GMD, terakhir diperbarui:03/06/2008 | ||
Untuk informasi lebih lanjut silahkan unduh lembar data | |
 | S-Plastics Lexan DMX6014.pdf |