SabikLexanDMX1214resin adalahaliran yang lebih baik, resin copolycarbonate transparan dengan ketahanan goresan yang lebih baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 77 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 92 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2830 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 116 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2630 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 77 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 62 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 101 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2310 | MPa | ISO 178 |
| Tes Kekerasan Pensil, 1kgf | F | - | ASTM D 3363 |
| kedalaman goresan Erichson, 6N | 14 | Mikrometer | Metode S-Plastics |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 32 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 68 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | 93 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 133 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 142 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 121 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Volume Spesifik | 0.85 | cm3/g | ASTM D 792 |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.1 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.3 | % | ASTM D 570 |
| Absorpsi air, 50% RH, keseimbangan | 0.14 | % | ASTM D 570 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.05 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 17.1 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.3 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 16 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | <0.8 | % | ASTM D 1003 |
| Indeks Refraksi | 1.584 | - | ASTM D 542 |
| Indeks Refraksi | 1.584 | - | ISO 489 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:03/27/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Sumber GMD, terakhir diperbarui:03/27/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan DMX1214.pdf |
|