S-Plastics LexanFXM173Rresin adalah UV stabil PC dalam efek khusus warna logam dan mutiara aditif warna dapat mempengaruhi kinerja
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2340 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2360 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 63 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 82 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 47 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 145 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 125 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.4E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 139 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 141 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 25 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.35 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 26 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:11/16/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 270 - 295 | °C |
| Suhu Nozzle | 265 - 290 | °C |
| Suhu depan - Zona 3 | 270 - 295 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 270 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:11/16/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan FXM173R.pdf |
|