S-Plastics LexanFXG154resin FXG154 adalah kelas Lexan PC dengan efek Diamond.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 57 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 5.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 39 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2680 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 98 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2390 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 61 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6.2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 75 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2430 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2340 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 752 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 142 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 62 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 51 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 16 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 153 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 147 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 149 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 129 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 2.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.15 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 2 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:03/14/2007 | |||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Kandungan Kelembaban Minimal | 0.01 | % |
| Suhu Peleburan (Parison) | 265 - 280 | °C |
| Barel - Zona 1 Suhu | 260 - 290 | °C |
| Barel - Zona 2 Suhu | 260 - 290 | °C |
| Barel - Zona 3 Suhu | 260 - 290 | °C |
| Barel - Zona 4 Suhu | 260 - 290 | °C |
| Adaptor - Zona 5 Suhu | 260 - 290 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Sumber GMD, terakhir diperbarui:03/14/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan EXRL0687.pdf |
|