S-Plastics Lexan HPX4EU resin adalah.Polikarbonat khusus aliran menengah - peningkatan proses dan autoclavability.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 131.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2210 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2210 | MPa | ASTM D 790 |
| Kekerasan, Rockwell L | 89 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 57 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 61 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 124.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2150 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 890 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 795 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 82 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 85 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat A/50 | 141 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 124 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 7.15E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 7.93E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 7.15E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.93E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 142 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.19 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.24 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 9 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 82 | % | ASTM D 1003 |
| Kabut | 3 | % | ASTM D 1003 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94V-2 Flame Class Rating (3) | 2.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 3 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 0,8 mm | 825 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 825 | °C | IEC 60695-2-13 |
| Sumber GMD, terakhir diperbarui:10/15/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 290 - 310 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 280 - 305 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 295 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:10/15/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan HPX4EU.pdf |
|