S-Plastics LexanHPH4704 resin adalah.Polikarbonat khusus panas tinggi. Untuk perangkat medis dan aplikasi farmasi. Manajemen perubahan perawatan kesehatan,biokompatibel (ISO10993 atau USP Kelas VI). EtO, uap,sterilisasi sinar gamma dan sinar e.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 77 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 78 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2330 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 92 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 127 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 68 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 68 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 102 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2170 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 66 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2070 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3200 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 370 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 84 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 577 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 149 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 74 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 173 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 148 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.21 | W/m-°C | ASTM C 177 |
| CTE, -40°C sampai 40°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 165 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 167 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 150 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
| Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.19 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.8 - 1 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 2 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.16 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.35 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 2 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 85 | % | ASTM D 1003 |
| Kabut | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.6 | - | ASTM D 542 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | > 2.5E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 20 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.27 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.1 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0016 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.026 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:08/21/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 370 | °C |
| Suhu Nozzle | 345 - 365 | °C |
| Suhu depan - Zona 3 | 350 - 370 | °C |
| Tengah - Zona 2 Suhu | 340 - 360 | °C |
| Bagian belakang - Zona 1 Suhu | 325 - 350 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:08/21/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan HPH4704.pdf |
|