S-Plastics LexanHPB3144G resin adalahAliran standar, transparan, resin kopolymer polikarbonat kemurnian tinggi dengan permeabilitas oksigen yang rendah dan tingkat transmisi uap air.Manajemen perubahan perawatan kesehatan, biokompatibel (ISO 10993 atau Kelas USP
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 80 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 70 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2900 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2600 | MPa | ASTM D 790 |
| Kekerasan, Rockwell L | 108 | - | ASTM D 785 |
| Kekerasan, Rockwell M | 93 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 40 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2450 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 108 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2450 | MPa | ISO 178 |
| Kekerasan, H358/30 | 128 | MPa | ISO 2039-1 |
| Tes Kekerasan Pensil, 1kgf | H | - | ASTM D 3363 |
| kedalaman goresan Erichson, 6N | 14 | Mikrometer | Metode S-Plastics |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 30 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 30 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 30 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | 45 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 47 | kJ/m2 | ISO 180/1U |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 47 | kJ/m2 | ISO 179/1eU |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 47 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 139 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 119 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 133 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 119 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.4 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 140 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 131 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 118 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.85 | cm3/g | ASTM D 792 |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.28 | % | ASTM D 570 |
| Absorpsi air, 50% RH, keseimbangan | 0.13 | % | ASTM D 570 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.04 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 14.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.27 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 13 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi cahaya, 2,54 mm | 88 | % | ASTM D 1003 |
| Kabut, 2,54 mm | <0.8 | % | ASTM D 1003 |
| Indeks Refraksi | 1.584 | - | ASTM D 542 |
| Indeks Refraksi | 1.584 | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.8 | - | ASTM D 150 |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Sumber GMD, terakhir diperbarui:2010/07/06 | |||
| Parameter | |
| Pencetakan Injeksi | Nilai |
| Suhu Pengeringan | 120 |
| Waktu Pengeringan | 3 - 4 |
| Kandungan Kelembaban Maksimal | 0.02 |
| Suhu Peleburan | 295 - 315 |
| Suhu Nozzle | 290 - 310 |
| Suhu depan - Zona 3 | 295 - 315 |
| Tengah - Zona 2 Suhu | 280 - 305 |
| Bagian belakang - Zona 1 Suhu | 260 - 280 |
| Suhu Hopper | 60 - 80 |
| Suhu Cetakan | 70 - 95 |
| Sumber GMD, terakhir diperbarui:2010/07/06 | |
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |