S-Plastics Lexan4404resin adalahCopolymer polikarbonat panas tinggi, dengan HDT 287F pada 264 psi.2008 kelas ini tidak boleh digunakan untuk aplikasi medis yang membutuhkan biokompatibilitas. Kelas alternatif HPH4404
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 66 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 70 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | > 50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2200 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 85 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2150 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 600 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 120 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*3 +23°C | 53 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 11 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 57 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 166 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 148 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 142 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 155 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 157 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 149 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 137 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.6 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0 - 0.2 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 6 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.16 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.35 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 330°C/2,16kg | 29 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:10/17/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 290 - 320 | °C |
| Suhu Nozzle | 280 - 310 | °C |
| Suhu depan - Zona 3 | 290 - 320 | °C |
| Tengah - Zona 2 Suhu | 280 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 270 - 300 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 120 | °C |
| Sumber GMD, terakhir diperbarui:10/17/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan 4404.pdf |
|