S-Plastics Lexan500resin adalah10% GR PC. Kombinasi optimal modulus tinggi ditambah kekuatan dampak yang sangat baik dan tahan api.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 66 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 15 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 103 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3440 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 85 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 124 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 2136 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 157 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 101 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 146 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 142 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 3.24E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.21 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
| Indeks suhu relatif, Elec | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Volume Spesifik | 0.8 | cm3/g | ASTM D 792 |
| Kepadatan | 1.245 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.12 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.31 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 7.5 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 17.7 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.1 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.05 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0008 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.0075 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 7 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.52 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3.04 | mm | UL 94 |
| CSA (Lihat File untuk daftar lengkap) | LS88480 | File No. | CSA terdaftar |
| Indeks Oksigen (LOI) | 36 | % | ASTM D 2863 |
| Daftar Panel Radiant | Ya. | - | Uji UL |
| Sinar UV, paparan air/pencelupan | F2 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 330 | °C |
| Suhu Nozzle | 305 - 325 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 300 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan 500.pdf |
|