S-Plastics Lexan194resin adalahNon-halogenated. 8.5 MFR. dampak tinggi. bagian dinding tebal. opaque saja. FDA sesuai kontak makanan dalam warna terbatas.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 115 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 81 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2130 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 68 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 747 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 420 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 169 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 126 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 6.48E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Volume Spesifik | 0.84 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.19 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.37 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 100°C | 0.54 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 8.5 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.5E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 16.3 | kV/mm | ASTM D 149 |
| Permittivitas Relatif, 1 MHz | 3 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:01/03/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 330 | °C |
| Suhu Nozzle | 305 - 325 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 300 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/03/2006 | ||
Untuk informasi lebih lanjut silahkan unduh lembar data | |
 | S-Plastics Lexan 194.pdf |