S-Plastics Lexan151Rresin adalahResin Lexan 151R adalah resin nonhalogenasi dengan viskositas tinggi yang dirancang untuk menjadi kandidat untuk aplikasi yang diproduksi melalui proses ekstrusi atau blow molding.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 70 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 747 | J/m | ASTM D 256 |
| Dampak tarik, tipe S | 630 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 169 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 6.84E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.19 | W/m-°C | ASTM C 177 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
| Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.35 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 100°C | 0.58 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 2.5 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Transmisi cahaya, 2,54 mm | 88 | % | ASTM D 1003 |
| Kabut, 2,54 mm | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.586 | - | ASTM D 542 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 14.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.17 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.96 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:2009/07/20 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 320 - 345 | °C |
| Suhu Nozzle | 315 - 340 | °C |
| Suhu depan - Zona 3 | 320 - 345 | °C |
| Tengah - Zona 2 Suhu | 310 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 300 - 320 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Kandungan Kelembaban Minimal | 0.01 | % |
| Suhu Peleburan (Parison) | 265 - 280 | °C |
| Barel - Zona 1 Suhu | 260 - 290 | °C |
| Barel - Zona 2 Suhu | 260 - 290 | °C |
| Barel - Zona 3 Suhu | 260 - 290 | °C |
| Barel - Zona 4 Suhu | 260 - 290 | °C |
| Adaptor - Zona 5 Suhu | 260 - 290 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Sumber GMD, terakhir diperbarui:2009/07/20 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Lexan 151R.pdf |
|