SabikColorcompWX96084resin adalahsenyawa yang didasarkan pada resin polibutilen terefalat.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 46 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 26.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 63 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 140 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 1.13E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 2.3 | % | Metode S-Plastics |
| Kepadatan | 1.5 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:12/11/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 240 - 265 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:12/11/2007 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics WX96084.pdf |
|